Evaluation of mechanical properties and water vapor permeability in Chitosan biofilms using Sorbitol and Glycerol

Abstract

Chitosan biofilms were prepared with and without plasticizer (glycerol and sorbitol). The physical and mechanical properties of chitosan biofilms with and without plasticizer were evaluated. Chitosan was obtained from shrimp wastes and characterized. The film forming solution (FFS) was obtained through chitosan dissolution and drying. The solution had its pH adjusted to 6.0 and oven dried (40 8C, 24 h) with forced air circulation. Chitosan biofilms without plasticizer showed a tensile strength about 36% higher than biofilms produced with plasticizer. On the other hand, biofilms with plasticizer presented superior values of elongation. The permeability of the water vapor and color presented significant difference (p<0.05) between all biofilms. Chitosan/plasticizer biofilms showed higher values of water vapor permeability in relation to chitosan biofilms without plasticizer.